How to control the hardness of industrial aluminum profiles in production?

Update time : 2022-09-07 19:01:00

Industrial aluminum profile in the production and processing, how to control the hardness is a key step, a little unqualified, will bring trouble to customers, so how to solve the industrial aluminum profile hard too low?

1, aluminum aging furnace temperature setting and control: usually, aging furnace temperature and aging furnace surface temperature will have a certain error, set the furnace surface temperature according to the actual temperature of the furnace to set, and pay close attention to the aging furnace temperature fluctuations.

2. Aluminum aging: aging should be carried out in strict accordance with the process requirements, and the holding time should be appropriate to prevent insufficient aging or over-aging resulting in insufficient hardness.

3, aluminum extrusion frame can not be too dense, there should be a gap between the material and the material, especially not ventilated small material, thick material interval is larger, tube material and small material, sheet material together in a frame, tube material put below this helps to circulate air supply.

4. Before aluminum profile loading, other special alloys of 6XXX and ordinary 6063 alloy should be aging separately. When aging with the same furnace is indeed required for production reasons, the process of special alloy should be used for aging. Extruded aluminum profile, without aging before the hardness is low, can not be used as a finished product, therefore, generally speaking, must be through aging to improve the strength.

Previous : How to reduce the scrap rate of aluminum profiles and improve the yield?

Next : What are the applications of aluminum veneer in interior decoration?

How to assemble and debug door and window aluminum profiles?

Jul .28.2023

The assembly and debugging of door and window aluminum profiles is one of the key links in the process of making doors and windows.

How to do a good job of cleaning industrial aluminum profiles?

Jul .17.2023

Spraying cleaning method of industrial aluminum profiles is widely used, because of complex equipment, high process requirements, poor cleaning effect, then how to better do spray cleaning of industrial aluminum profiles?

Aluminum extrusion profile six places are required during the stretching process

Jul .07.2023

The aluminum extrusion profile must be cooled to below 50 degrees before stretching. If the temperature is too high, stretching will not only burn the human body, the hair belt, but also expose absolute waste products such as bending, twisting, and poor performance before and after aging, because the stress in the aluminum alloy profile can not be completely eliminated.

Curtain wall aluminum profile purchase mainly see where?

Jul .06.2023

Appearance quality of curtain wall aluminum profile: the surface of anodic oxide film is not allowed to have electrical burns, oxide film falling off and other defects; Electrophoretic, powder, fluorocarbon profile paint film should be uniform, neat, smooth, do not allow wrinkles, cracks, bubbles, flow signs, inclusions and paint film fall off and other defects, but allow local film within 80 mm at the end of the profile.

Hammy Han